Facile Preparation of Highly Monodisperse Small Silica Spheres (15 to >200 nm) Suitable for Colloidal Templating and Formation of Ordered Arrays

Langmuir ◽  
2008 ◽  
Vol 24 (5) ◽  
pp. 1714-1720 ◽  
Author(s):  
Kurtis D. Hartlen ◽  
Aristidis P. T. Athanasopoulos ◽  
Vladimir Kitaev
Keyword(s):  
Silica Spheres ◽  
Ordered Arrays ◽  
Colloidal Templating ◽  
Facile Preparation

RNA polymerase: Preparation and structural analysis of helical polymers

1984 ◽  
Vol 42 ◽  
pp. 152-153
Author(s):  
E. Loren Buhle ◽  
Pamela Rew ◽  
Ueli Aebi
Keyword(s):  
Structural Analysis ◽  
Rna Polymerase ◽  
Molecular Level ◽  
X Ray Diffraction ◽  
Helical Polymers ◽  
X Ray ◽  
E Coli ◽  
The Past ◽  
Ordered Arrays ◽  
Low Ionic Strength

While DNA-dependent RNA polymerase represents one of the key enzymes involved in transcription and ultimately in gene expression in procaryotic and eucaryotic cells, little progress has been made towards elucidation of its 3-D structure at the molecular level over the past few years. This is mainly because to date no 3-D crystals suitable for X-ray diffraction analysis have been obtained with this rather large (MW ~500 kd) multi-subunit (α2ββ'ζ). As an alternative, we have been trying to form ordered arrays of RNA polymerase from E. coli suitable for structural analysis in the electron microscope combined with image processing. Here we report about helical polymers induced from holoenzyme (α2ββ'ζ) at low ionic strength with 5-7 mM MnCl2 (see Fig. 1a). The presence of the ζ-subunit (MW 86 kd) is required to form these polymers, since the core enzyme (α2ββ') does fail to assemble into such structures under these conditions.

Facile preparation of nanofiller-paper using mixed office paper without deinking

TAPPI Journal ◽  
2015 ◽  
Vol 14 (3) ◽  
pp. 167-174 ◽  
Author(s):  
QIANQIAN WANG ◽  
J.Y. ZHU
Keyword(s):  
Cellulose Nanofibrils ◽  
Ash Content ◽  
Raw Material ◽  
Mechanical Grinding ◽  
Microscope Imaging ◽  
Facile Preparation ◽  
Electron Microscope Imaging ◽  
Thermal Stability Of ◽  
Scanning Electron ◽  
Office Paper

Mixed office paper (MOP) pulp without deinking with an ash content of 18.1 ± 1.5% was used as raw material to produce nanofiller-paper. The MOP pulp with filler was mechanically fibrillated using a laboratory stone grinder. Scanning electron microscope imaging revealed that the ground filler particles were wrapped by cellulose nanofibrils (CNFs), which substantially improved the incorporation of filler into the CNF matrix. Sheets made of this CNF matrix were densified due to improved bonding. Specific tensile strength and modulus of the nanofiller-paper with 60-min grinding reached 48.4 kN·m/kg and 8.1 MN·m/kg, respectively, approximately 250% and 200% of the respective values of the paper made of unground MOP pulp. Mechanical grinding duration did not affect the thermal stability of the nanofiller-paper.

Sign in / Sign up

Export Citation Format

Share Document