Synthesis, Crystal Structure, and Characterization (Vibrational and Solid-State31P MAS NMR Spectroscopy) of the High-Temperature Modification of Calciumcatena-Polyphosphate(V)

2007 ◽  
Vol 19 (21) ◽  
pp. 5067-5073 ◽  
Author(s):  
Matthias Weil ◽  
Michael Puchberger ◽  
Jörn Schmedt auf der Günne ◽  
Johannes Weber
Keyword(s):  
Crystal Structure ◽  
High Temperature ◽  
Nmr Spectroscopy ◽  
Mas Nmr ◽  
Temperature Modification ◽  
High Temperature Modification

Zur Kenntnis des Argyrodit-Strukturtyps: Die Kristallstruktur von Ag8SiS6 / The Argyrodite Structure Type : The Crystal Structure of Ag8SiS6

1977 ◽  
Vol 32 (4) ◽  
pp. 373-379 ◽  
Author(s):  
Bernt Krebs ◽  
Jürgen Mandt
Keyword(s):  
Crystal Structure ◽  
High Temperature ◽  
Room Temperature ◽  
Structure Type ◽  
Orthorhombic Space Group ◽  
X Ray ◽  
Temperature Modification ◽  
Face Centered ◽  
Temperature Factors ◽  
High Temperature Modification

The room temperature modification of Ag8SiS6 is orthorhombic, space group Pna21, with α = 15.024, b = 7.428, c = 10.533 Å, Z = 4. A complete single crystal X-ray structure analysis shows the structure to contain tetrahedral SiS4(4-) units (Si-S 2.094(12) ... 2.130(12) Å) besides isolated sulfide groups coordinated by Ag; the compound may thus be formulated as Ag8(SiS4)(S)2. The coordination of the Ag atoms by sulfur is distorted tetrahedral (Ag-S 2.557...2.757 A), approximately trigonal planar (Ag-S 2.386...2.775 A, with one additional weakly bonded axial S at 2.991 ... 3.330 Å), or linear (Ag-S 2.414... 2.443 Å). Within the (ordered) Ag sublattice the temperature factors are significantly higher than for Si and S, indicating a certain mobility of the Ag atoms. The arrangement of the thiosilicate -sulfide part of the structure is pseudocubic face-centered, showing the close structural relationship to the disordered cubic high temperature modification of Ag8GeTe6.