scholarly journals Diagnosis of carbonation induced corrosion initiation and progression in reinforced concrete structures using piezo-impedance transducers

2016 ◽  
Vol 242 ◽  
pp. 79-91 ◽  
Author(s):  
V. Talakokula ◽  
S. Bhalla ◽  
R.J. Ball ◽  
C.R. Bowen ◽  
G.L. Pesce ◽  
...  
Keyword(s):  
Reinforced Concrete ◽  
Concrete Structures ◽  
Reinforced Concrete Structures ◽  
Corrosion Initiation

scholarly journals Experimental and Empirical Time to Corrosion of Reinforced Concrete Structures under Different Curing Conditions

2014 ◽  
Vol 2014 ◽  
pp. 1-9 ◽  
Author(s):  
Ahmed A. Abouhussien ◽  
Assem A. A. Hassan
Keyword(s):  
Reinforced Concrete ◽  
Corrosion Test ◽  
Concrete Structures ◽  
Reinforced Concrete Structures ◽  
Cell Potential ◽  
Accelerated Corrosion ◽  
Curing Conditions ◽  
Expected Time ◽  
Corrosion Initiation ◽  
Accelerated Corrosion Test

Reinforced concrete structures, especially those in marine environments, are commonly subjected to high concentrations of chlorides, which eventually leads to corrosion of the embedded reinforcing steel. The total time to corrosion of such structures may be divided into three stages: corrosion initiation, cracking, and damage periods. This paper evaluates, both empirically and experimentally, the expected time to corrosion of reinforced concrete structures. The tested reinforced concrete samples were subjected to ten alternative curing techniques, including hot, cold, and normal temperatures, prior to testing. The corrosion initiation, cracking, and damage periods in this investigation were experimentally monitored by an accelerated corrosion test performed on reinforced concrete samples. Alternatively, the corrosion initiation time for counterpart samples was empirically predicted using Fick’s second law of diffusion for comparison. The results showed that the corrosion initiation periods obtained experimentally were comparable to those obtained empirically. The corrosion initiation was found to occur at the first jump of the current measurement in the accelerated corrosion test which matched the half-cell potential reading of around −350 mV.