scholarly journals Atomic segregation at twin boundaries in a Mg-Ag alloy

2020 ◽  
Vol 178 ◽  
pp. 193-197 ◽  
Author(s):  
X.F. Chen ◽  
L.R. Xiao ◽  
Z.G. Ding ◽  
W. Liu ◽  
Y.T. Zhu ◽  
...  
Keyword(s):  
Twin Boundaries ◽  
Atomic Segregation

Arsenic segregation in polysilicon

1983 ◽  
Vol 41 ◽  
pp. 154-155 ◽  
Author(s):  
P.E. Batson ◽  
C.R.M. Grovenor ◽  
D.A. Smith ◽  
C. Wong
Keyword(s):  
Incident Beam ◽  
Silicon Wafers ◽  
Chemical Polishing ◽  
Bright Field Image ◽  
Beam Size ◽  
Stem Analysis ◽  
Bright Field ◽  
Twin Boundaries ◽  
X Ray ◽  
Line Scan

In this work As doped polysilicon was deposited onto (100) silicon wafers by APCVD at 660°C from a silane-arsine mixture, followed by a ten minute anneal at 1000°C, and in one case a further ten minute anneal at 700°C. Specimens for TEM and STEM analysis were prepared by chemical polishing. The microstructure, which is unchanged by the final 700°C anneal,is shown in Figure 1. It consists of numerous randomly oriented grains many of which contain twins.X-ray analysis was carried out in a VG HB5 STEM. As K α x-ray counts were collected from STEM scans across grain and twin boundaries, Figures 2-4. The incident beam size was about 1.5nm in diameter, and each of the 20 channels in the plots was sampled from a 1.6nm length of the approximately 30nm line scan across the boundary. The bright field image profile along the scanned line was monitored during the analysis to allow correlation between the image and the x-ray signal.

Measurement of the Displacement Across a Coincidence Grain Boundary

1977 ◽  
Vol 35 ◽  
pp. 124-125
Author(s):  
J. W. Matthews ◽  
W. M. Stobbs
Keyword(s):  
Grain Boundary ◽  
Grain Boundaries ◽  
Stacking Fault ◽  
The Other ◽  
Measuring Technique ◽  
High Angle ◽  
Twin Boundaries ◽  
Rigid Displacement ◽  
Cubic Crystals ◽  
Lattice Displacement

Many high-angle grain boundaries in cubic crystals are thought to be either coincidence boundaries (1) or coincidence boundaries to which grain boundary dislocations have been added (1,2). Calculations of the arrangement of atoms inside coincidence boundaries suggest that the coincidence lattice will usually not be continuous across a coincidence boundary (3). There will usually be a rigid displacement of the lattice on one side of the boundary relative to that on the other. This displacement gives rise to a stacking fault in the coincidence lattice.Recently, Pond (4) and Smith (5) have measured the lattice displacement at coincidence boundaries in aluminum. We have developed (6) an alternative to the measuring technique used by them, and have used it to find two of the three components of the displacement at {112} lateral twin boundaries in gold. This paper describes our method and presents a brief account of the results we have obtained.

Observation by HVEM of the martensite transformation and the superconducting transition in Nb3Sn

1988 ◽  
Vol 46 ◽  
pp. 788-789
Author(s):  
M. A. Kirk ◽  
M. C. Baker ◽  
B. J. Kestel ◽  
H. W. Weber
Keyword(s):  
Thin Films ◽  
Low Temperature ◽  
Superconducting State ◽  
Martensite Transformation ◽  
Sputter Deposition ◽  
Diffusion Reaction ◽  
Solute Diffusion ◽  
Superconducting Transition ◽  
Twin Boundaries ◽  
Martensite Structure

It is well known that a number of compound superconductors with the A15 structure undergo a martensite transformation when cooled to the superconducting state. Nb3Sn is one of those compounds that transforms, at least partially, from a cubic to tetragonal structure near 43 K. To our knowledge this transformation in Nb3Sn has not been studied by TEM. In fact, the only low temperature TEM study of an A15 material, V3Si, was performed by Goringe and Valdre over 20 years ago. They found the martensite structure in some foil areas at temperatures between 11 and 29 K, accompanied by faults that consisted of coherent twin boundaries on {110} planes. In pursuing our studies of irradiation defects in superconductors, we are the first to observe by TEM a similar martensite structure in Nb3Sn.Samples of Nb3Sn suitable for TEM studies have been produced by both a liquid solute diffusion reaction and by sputter deposition of thin films.

Carbide precipitation and chromium depletion on coherent twin boundaries in deformed 304 stainless steels

1992 ◽  
Vol 50 (2) ◽  
pp. 1216-1217
Author(s):  
A.H. Advani ◽  
L.E. Murr ◽  
D.J. Matlock ◽  
W.W. Fisher ◽  
P.M. Tarin ◽  
...  
Keyword(s):  
Grain Boundaries ◽  
Stainless Steels ◽  
Interfacial Free Energy ◽  
Carbide Precipitation ◽  
Twin Boundaries ◽  
Invariant Structure ◽  
Heat Treated ◽  
Constant Structure ◽  
Cr Depletion

Coherent annealing-twin boundaries are constant structure and energy interfaces with an average interfacial free energy of ∼19mJ/m2 versus ∼210 and ∼835mJ/m2 for incoherent twins and “regular” grain boundaries respectively in 304 stainless steels (SS). Due to their low energy, coherent twins form carbides about a factor of 100 slower than grain boundaries, and limited work has also shown differences in Cr-depletion (sensitization) between twin versus grain boundaries. Plastic deformation, may, however, alter the kinetics and thermodynamics of twin-sensitization which is not well understood. The objective of this work was to understand the mechanisms of carbide precipitation and Cr-depletion on coherent twin boundaries in deformed SS. The research is directed toward using this invariant structure and energy interface to understand and model the role of interfacial characteristics on deformation-induced sensitization in SS. Carbides and Cr-depletion were examined on a 20%-strain, 0.051%C-304SS, heat treated to 625°C-4.5h, as described elsewhere.

Interfacial dislocation arrays in twin boundaries of deformed titanium

1994 ◽  
Vol 30 (10) ◽  
pp. 1311-1315 ◽  
Author(s):  
Th. Kehagias ◽  
Ph. Komninou ◽  
G.P. Dimitrakopulos ◽  
J.G. Antonopoulos ◽  
Th. Karakostas
Keyword(s):  
Twin Boundaries ◽  
Interfacial Dislocation ◽  
Dislocation Arrays

scholarly journals Structural Transformations and Mechanical Properties of Metastable Austenitic Steel under High Temperature Thermomechanical Treatment

Metals ◽  
2021 ◽  
Vol 11 (4) ◽  
pp. 645
Author(s):  
Igor Litovchenko ◽  
Sergey Akkuzin ◽  
Nadezhda Polekhina ◽  
Kseniya Almaeva ◽  
Evgeny Moskvichev
Keyword(s):  
Plastic Deformation ◽  
Grain Size ◽  
High Temperature ◽  
Austenitic Steel ◽  
Structural Transformations ◽  
Initial State ◽  
Twin Boundaries ◽  
Metastable Austenitic Steel ◽  
Average Grain Size ◽  
Heating Up

The effect of high-temperature thermomechanical treatment on the structural transformations and mechanical properties of metastable austenitic steel of the AISI 321 type is investigated. The features of the grain and defect microstructure of steel were studied by scanning electron microscopy with electron back-scatter diffraction (SEM EBSD) and transmission electron microscopy (TEM). It is shown that in the initial state after solution treatment the average grain size is 18 μm. A high (≈50%) fraction of twin boundaries (annealing twins) was found. In the course of hot (with heating up to 1100 °C) plastic deformation by rolling to moderate strain (e = 1.6, where e is true strain) the grain structure undergoes fragmentation, which gives rise to grain refining (the average grain size is 8 μm). Partial recovery and recrystallization also occur. The fraction of low-angle misorientation boundaries increases up to ≈46%, and that of twin boundaries decreases to ≈25%, compared to the initial state. The yield strength after this treatment reaches up to 477 MPa with elongation-to-failure of 26%. The combination of plastic deformation with heating up to 1100 °C (e = 0.8) and subsequent deformation with heating up to 600 °C (e = 0.7) reduces the average grain size to 1.4 μm and forms submicrocrystalline fragments. The fraction of low-angle misorientation boundaries is ≈60%, and that of twin boundaries is ≈3%. The structural states formed after this treatment provide an increase in the strength properties of steel (yield strength reaches up to 677 MPa) with ductility values of 12%. The mechanisms of plastic deformation and strengthening of metastable austenitic steel under the above high-temperature thermomechanical treatments are discussed.

The effect of HCP on the formation of twin boundaries and dislocations in Ni–Co alloys

2021 ◽  
Vol 29 ◽  
pp. 18-23
Author(s):  
Rui-bo Ma ◽  
Li-li Zhou ◽  
Yong-chao Liang ◽  
Qian Chen ◽  
Ze-an Tian ◽  
...  
Keyword(s):  
Twin Boundaries ◽  
Co Alloys
Sign in / Sign up

Export Citation Format

Share Document