New insights into the mechanism of low-temperature active-screen plasma nitriding of austenitic stainless steel

2012 ◽  
Vol 67 (1) ◽  
pp. 89-91 ◽  
Author(s):  
S. Corujeira Gallo ◽  
H. Dong
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Low Temperature ◽  
Plasma Nitriding ◽  
Active Screen Plasma Nitriding ◽  
Active Screen

scholarly journals Application of Active-Screen Plasma Nitriding to an Austenitic Stainless Steel Small-Diameter Thin Pipe

Metals ◽  
2021 ◽  
Vol 11 (2) ◽  
pp. 366
Author(s):  
Kenzo Sumiya ◽  
Shinkichi Tokuyama ◽  
Akio Nishimoto ◽  
Junichi Fukui ◽  
Atsushi Nishiyama
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
Austenitic Stainless Steel ◽  
Low Temperature ◽  
Plasma Nitriding ◽  
Small Diameter ◽  
Surface Hardness ◽  
Bending Rigidity ◽  
Nitriding Temperature ◽  
Active Screen Plasma Nitriding

Low-temperature active-screen plasma nitriding (ASPN) was applied in this study to improve the bending rigidity and corrosion resistance of a small-diameter thin pipe composed of austenitic stainless steel (SUS 304). The inner and outer diameters of the pipe were ϕ0.3 and ϕ0.4 mm, respectively, and the pipe length was 50 mm. The jig temperature was measured using a thermocouple and was adopted as the nitriding temperature because measuring the temperature of a small-diameter pipe is difficult. The nitriding temperature was varied from 578 to 638 K to investigate the effect of temperature on the nitriding layer and mechanical property. The nitriding layer thickness increased with an increase in nitriding temperature, reaching 15 μm at 638 K. The existence of expanded austenite (S phase) in this nitriding layer was revealed using the X-ray diffraction pattern. Moreover, the surface hardness increased with the nitriding temperature and took a maximum value of 1100 HV above 598 K. The bending load increased with an increase in the nitriding temperature in relation to the thicker nitriding layer and increased surface hardness. The nitrided samples did not corrode near the center, and corrosion was noted only near the tip at high nitriding temperatures of 618 and 638 K in a salt spray test. These results indicated that the bending rigidity of the small-diameter thin pipe composed of austenitic stainless steel was successfully improved using low-temperature ASPN while ensuring corrosion resistance.

Low temperature active screen plasma nitriding of 17–4 PH stainless steel

2016 ◽  
Vol 308 ◽  
pp. 189-194 ◽  
Author(s):  
Carlos Eduardo Pinedo ◽  
Sharys Ivonn Varela Larrotta ◽  
Arthur Seiji Nishikawa ◽  
Hanshan Dong ◽  
Xiao-Ying Li ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Low Temperature ◽  
Plasma Nitriding ◽  
Active Screen Plasma Nitriding ◽  
Active Screen
Sign in / Sign up

Export Citation Format

Share Document