Using polycrystal plasticity modeling to determine the effects of grain size and solid solution additions on individual deformation mechanisms in cast Mg alloys

2010 ◽  
Vol 63 (7) ◽  
pp. 731-736 ◽  
Author(s):  
Babak Raeisinia ◽  
Sean R. Agnew
Keyword(s):  
Solid Solution ◽  
Grain Size ◽  
Mg Alloys ◽  
Deformation Mechanisms ◽  
Polycrystal Plasticity

Dislocation Plasticity and Complementary Deformation Mechanisms in Polycrystalline Mg Alloys

2004 ◽  
Vol 449-452 ◽  
pp. 665-668 ◽  
Author(s):  
Junichi Koike
Keyword(s):  
Grain Size ◽  
Grain Boundary ◽  
Deformation Mechanism ◽  
Room Temperature ◽  
Grain Boundary Sliding ◽  
Mg Alloys ◽  
Deformation Mechanisms ◽  
Slip Systems ◽  
Dislocation Plasticity ◽  
Boundary Sliding

Deformation mechanisms of Mg-Al-Zn (AZ31) alloys were investigated by performing tensile test at room temperature. In fine grain Mg alloys deformed at room temperature, nonbasal slip systems were found to be active as well as basal slip systems because of grain-boundary compatibility effect. Slip-induced grain-boundary sliding occurred as a complementary deformation mechanism to give rise to c-axis component of strain. With increasing grain size, the activation of the nonbasal slip systems was limited near grain boundaries. Instead of grain-boundary sliding, twinning occurred as a complementary deformation mechanism in large grained samples. Orientation analysis of twins indicated that twinning is induced by stress concentration due to the pile up of basal dislocations. The grain-size dependence on deformation mechanism was found to affect yielding behavior both microscopically and macroscopically which can influence various mechanical properties such as fatigue and creep.

scholarly journals Creep Deformation Mechanisms in Coarse-Grained Solid Solution Mg Alloys

2004 ◽  
Vol 45 (4) ◽  
pp. 1266-1271 ◽  
Author(s):  
Sung Wook Chung ◽  
Hiroyuki Watanabe ◽  
Woo-Jin Kim ◽  
Kenji Higashi
Keyword(s):  
Solid Solution ◽  
Creep Deformation ◽  
Mg Alloys ◽  
Deformation Mechanisms ◽  
Coarse Grained

scholarly journals Al, Cu and Zr Addition to High Entropy Alloys: The Effect on Recrystallization Temperature

2018 ◽  
Vol 941 ◽  
pp. 1137-1142
Author(s):  
Elena Colombini ◽  
Andrea Garzoni ◽  
Roberto Giovanardi ◽  
Paolo Veronesi ◽  
Angelo Casagrande
Keyword(s):  
Solid Solution ◽  
Grain Size ◽  
Single Phase ◽  
Boundary Energy ◽  
Cold Deformation ◽  
Recrystallization Temperature ◽  
High Entropy Alloys ◽  
High Entropy ◽  
Ni Alloy ◽  
Sluggish Diffusion

The equimolar Cr, Mn, Fe, Co and Ni alloy, first produced in 2004, was unexpectedly found to be single-phase. Consequently, a new concept of materials was developed: high entropy alloys (HEA) forming a single solid-solution with a near equiatomic composition of the constituting elements. In this study, an equimolar CoCrFeMnNi HEA was modified by the addition of 5 at% of either Al, Cu or Zr. The cold-rolled alloys were annealed for 30 minutes at high temperature to investigate the recrystallization kinetics. The evolution of the grain boundary and the grain size were investigated, from the as-cast to the recrystallized state. Results show that the recrystallized single phase FCC structures exhibits different twin grains density, grain size and recrystallization temperatures as a function of the at.% of modifier alloying elements added. In comparison to the equimolar CoCrFeMnNi, the addition of modifier elements increases significantly the recrystallization temperature after cold deformation. The sluggish diffusion (typical of HEA alloys), the presence of a solute in solid solution as well as the low twin boundary energy are responsible for the lower driving force for recrystallization.

scholarly journals Effect of Rare Earth Ce on Deep Stamping Properties of High-Strength Interstitial-Free Steel Containing Phosphorus

Materials ◽  
2020 ◽  
Vol 13 (6) ◽  
pp. 1473
Author(s):  
Hao Wang ◽  
Yanping Bao ◽  
Chengyi Duan ◽  
Lu Lu ◽  
Yan Liu ◽  
...  
Keyword(s):  
Solid Solution ◽  
Grain Size ◽  
Rare Earth ◽  
High Strength ◽  
Rolling Process ◽  
P Element ◽  
Second Phase ◽  
Strengthening Effect ◽  
Interstitial Free ◽  
If Steel

The influence of rare earth Ce on the deep stamping property of high-strength interstitial-free (IF) steel containing phosphorus was analyzed. After adding 120 kg ferrocerium alloy (Ce content is 10%) in the steel, the inclusion statistics and the two-dimensional morphology of the samples in the direction of 1/4 thickness of slab and each rolling process were observed and compared by scanning electron microscope (SEM). After the samples in each rolling process were treated by acid leaching, the three-dimensional morphology and components of the second phase precipitates were observed by SEM and energy dispersive spectrometer (EDS). The microstructure of the sample was observed by optical microscope, and the grain size was compared. Meanwhile, the content and strength of the favorable texture were analyzed by X-ray diffraction (XRD). Finally, the mechanical properties of the product were analyzed. The results showed that: (1) The combination of rare earth Ce with activity O and S in steel had lower Gibbs free energy, and it was easy to generate CeAlO3, Ce2O2S, and Ce2O3. The inclusions size was obviously reduced, but the number of inclusions was increased after adding rare earth. The morphology of inclusions changed from chain and strip to spherical. The size of rare earth inclusions was mostly about 2–5 μm, distributed and dispersed, and their elastic modulus was close to that of steel matrix, which was conducive to improving the structure continuity of steel. (2) The rare earth compound had a high melting point. As a heterogeneous nucleation point, the nucleation rate was increased and the solidification structure was refined. The grade of grain size of products was increased by 1.5 grades, which is helpful to improve the strength and plasticity of metal. (3) Rare earth Ce can inhibit the segregation of P element at the grain boundary and the precipitation of Fe(Nb+Ti)P phase. It can effectively increase the solid solution amount of P element in steel, improve the solid solution strengthening effect of P element in high-strength IF steel, and obtain a large proportion of {111} favorable texture, which is conducive to improving the stamping formability index r90 value.

Investigations on Microstructure Evolution and Deformation Behavior of Aged and Ultrafine Grained Al-Zn-Mg Alloy Subjected to Severe Plastic Deformation

2010 ◽  
Vol 667-669 ◽  
pp. 253-258
Author(s):  
Wei Ping Hu ◽  
Si Yuan Zhang ◽  
Xiao Yu He ◽  
Zhen Yang Liu ◽  
Rolf Berghammer ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Plastic Deformation ◽  
Grain Size ◽  
Severe Plastic Deformation ◽  
Microstructure Evolution ◽  
Deformation Behavior ◽  
Deformation Mechanisms ◽  
Mg Alloy ◽  
Ultrafine Grained

An aged Al-5Zn-1.6Mg alloy with fine η' precipitates was grain refined to ~100 nm grain size by severe plastic deformation (SPD). Microstructure evolution during SPD and mechanical behaviour after SPD of the alloy were characterized by electron microscopy and tensile, compression as well as nanoindentation tests. The influence of η' precipitates on microstructure and mechanical properties of ultrafine grained Al-Zn-Mg alloy is discussed with respect to their effect on dislocation configurations and deformation mechanisms during processing of the alloy.

The Influence of Section Thickness on Microstructure of Elektron 21 and QE22 Magnesium Alloys

2012 ◽  
Vol 191 ◽  
pp. 145-150 ◽  
Author(s):  
Michał Stopyra ◽  
Robert Jarosz ◽  
Andrzej Kiełbus
Keyword(s):  
Solid Solution ◽  
Grain Size ◽  
Magnesium Alloys ◽  
Statistical Methods ◽  
Wall Thickness ◽  
Light Microscope ◽  
Volume Fraction ◽  
Grain Structure ◽  
Section Thickness ◽  
Gating System

The paper presents analysis of section thickness’ influence on microstructure of Elektron 21 and QE22 magnesium alloys in the form of a stepped casting test. Solid solution grain size and volume fraction of eutectic areas were measured using light microscope and sterological methods. The results showed the significant increase of grain size caused by wall thickness and its slight decrease connected with the distance beetwen analysed section and the gating system. This relationship was confirmed using statistical methods. QE22 alloy demonstrated finer grain structure than Elektron 21 alloy as well as lesser susceptibility of grain size to solidification conditions

Ductile deformation and microstructures

2021 ◽  
pp. 58-85
Author(s):  
Jean-Luc Bouchez ◽  
Adolphe Nicolas
Keyword(s):  
Plastic Deformation ◽  
Grain Size ◽  
Elastic Deformation ◽  
Applied Stress ◽  
Deformation Mechanism ◽  
Chemical Elements ◽  
Shear Zones ◽  
Ductile Deformation ◽  
Deformation Mechanisms ◽  
Solid Materials

In contrast to the elastic deformation, which is reversible, usually neglected by field geologists but important for geophysicists working in seismology, ductile deformation is irreversible. This chapter is restricted to solid materials. Materials containing a melt fraction will be examined in Chapter 7. In the geological literature, ‘ductile’ is often used as a synonym for ‘plastic’. The latter is rather used, and will be used to specify deformation mechanisms that dominantly involve the action of dislocations. In contrast to brittle deformation, which by essence is discontinuous and highly localized (see Chapter 3), ductile deformation is generally continuous and affects large volumes of rock. However, ductile deformation may be concentrated into restricted rock volumes (or domains). Such localization is common in shear zones and/or when superplastic deformation mechanism is involved. Plastic deformation mechanisms naturally depend on temperature, magnitude of the applied stress, mineral nature and grain-size of the rocks. In upper parts of the crust, fluids are able to carry chemical elements over large distances and influence the deformation mechanisms. Micrographs of several microstructural types as well as deformation maps for olivine and calcite are given at the end of this chapter.

Sign in / Sign up

Export Citation Format

Share Document