Effect of in-situ heat treatments on deposition characteristics and mechanical properties for repairs using laser melting deposition

2020 ◽  
Vol 58 ◽  
pp. 1019-1033
Author(s):  
Wook Jin Oh ◽  
Yong Son ◽  
Shim Do Sik
Keyword(s):  
Mechanical Properties ◽  
Heat Treatments ◽  
Laser Melting ◽  
Laser Melting Deposition

Experiments and numerical simulations for the mechanical properties of Ni-based superalloys fabricated by laser melting deposition

2021 ◽  
Vol 140 ◽  
pp. 107058
Author(s):  
Jiaqi Zhang ◽  
Zhaozhen Huang ◽  
Yan Fang ◽  
Zhenjie Gu ◽  
Jichang Xie ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Numerical Simulations ◽  
Laser Melting ◽  
Laser Melting Deposition

scholarly journals In-situ reactions and mechanical properties of 6061 aluminum alloy weld joint with SiCp by laser melting injection

2021 ◽  
Vol 203 ◽  
pp. 109538
Author(s):  
Boan Xu ◽  
Ping Jiang ◽  
Shaoning Geng ◽  
Yilin Wang ◽  
Jintian Zhao ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Weld Joint ◽  
Laser Melting ◽  
6061 Aluminum Alloy ◽  
In Situ Reactions ◽  
Alloy Weld

Influence of Heat Treatment on Microstructure and Mechanical Properties of Selective Laser Melted TiAl6V4 Alloy

2018 ◽  
Vol 284 ◽  
pp. 615-620 ◽  
Author(s):  
R.M. Baitimerov ◽  
P.A. Lykov ◽  
L.V. Radionova
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Selective Laser Melting ◽  
Room Temperature ◽  
Base Alloy ◽  
Tensile Tests ◽  
Heat Treatments ◽  
Laser Melting ◽  
Microstructure And Mechanical Properties ◽  
Treatment Procedures

TiAl6V4 titanium base alloy is widely used in aerospace and medical industries. Specimens for tensile tests from TiAl6V4 with porosity less than 0.5% was fabricated by selective laser melting (SLM). Specimens were treated using two heat treatment procedures, third batch of specimens was tested in as-fabricated statement after machining. Tensile tests were carried out at room temperature. Microstructure and mechanical properties of SLM fabricated TiAl6V4 after different heat treatments were investigated.

scholarly journals Mechanical Properties of In-Situ Synthesis of Ti-Ti3Al Metal Composite Prepared by Selective Laser Melting

Metals ◽  
2019 ◽  
Vol 9 (10) ◽  
pp. 1121 ◽  
Author(s):  
Li ◽  
Liang ◽  
Tian ◽  
Yang ◽  
Xie ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Wear Resistance ◽  
Selective Laser Melting ◽  
Melting Process ◽  
In Situ Synthesis ◽  
Metal Composite ◽  
Dispersion Strengthening ◽  
Laser Melting ◽  
Compression Properties

Titanium composite strengthened by Ti3Al precipitations is considered to be one of the excellent materials that is widely used in engineering. In this work, we prepared a kind of Ti-Ti3Al metallic composite by in-situ synthesis technology during the SLM (selective laser melting) process, and analyzed its microstructure, wear resistance, microhardness, and compression properties. The results showed that the Ti-Ti3Al composite, prepared by in-situ synthesis technology based on SLM, had more homogeneous Ti3Al-enhanced phase dispersion strengthening structure. The grain size of the workpiece was about 1 μm, and that of the Ti3Al particle was about 200 nm. Granular Ti3Al was precipitated after the aluminum-containing workpiece formed, with a relatively uniform distribution. Regarding the mechanical properties, the hardness (539 HV) and the wear resistance were significantly improved when compared with the Cp-Ti workpiece. The compressive strength of the workpiece increased from 886.32 MPa to 1568 MPa, and the tensile strength of the workpiece increased from 531 MPa to 567 MPa after adding aluminum. In the future, the combination of in-situ synthesis technology and SLM technology can be used to flexibly adjust the properties of Ti-based materials.