Effects of heat treatment on the microstructure and mechanical properties of in situ inhomogeneous TiBw/Ti6Al4V composite fabricated by pre–sintering and canned powder extrusion

2017 ◽  
Vol 693 ◽  
pp. 1116-1123 ◽  
Author(s):  
Wencong Zhang ◽  
Yangju Feng ◽  
Wenzhen Chen ◽  
Janlei Yang
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Microstructure And Mechanical Properties

Microstructure and Mechanical Properties of TiB2/ Al-Si Composites Fabricated by TIG Wire and Arc Additive Manufacturing

2019 ◽  
Vol 944 ◽  
pp. 64-72
Author(s):  
Qing Feng Yang ◽  
Cun Juan Xia ◽  
Ya Qi Deng
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Additive Manufacturing ◽  
Yield Strength ◽  
Filler Wire ◽  
T6 Heat Treatment ◽  
Microstructure And Mechanical Properties ◽  
Before And After

Bulky sample was made by using TIG wire and arc additive manufacturing (WAAM) technology, in which Ф1.6 mm filler wire of in-situ TiB2/Al-Si composites was selected as deposition metal, following by T6 heat treatment. The microstructure and mechanical properties of the bulky sample before and after heat treatment were analyzed. Experimental results showed that the texture of the original samples parallel to the weld direction and perpendicular to the weld direction was similar consisting of columnar dendrites and equiaxed crystals. After T6 heat treatment, the hardness of the sample was increased to 115.85 HV from 62.83 HV, the yield strength of the sample was 273.33 MPa, the average tensile strength was 347.33 MPa, and the average elongation after fracture was 7.96%. Although pore defects existed in the fracture, yet the fracture of the sample was ductile fracture.

Effects of Rapid Heat Treatment on Microstructure and Mechanical Properties of Ti2AlC/TiAl Composite

2007 ◽  
Vol 336-338 ◽  
pp. 1164-1167
Author(s):  
Yun Long Yue ◽  
Hai Tao Wu ◽  
Wei Bing Wu ◽  
Hai Yan Yin
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Fracture Toughness ◽  
Bending Strength ◽  
Duplex Microstructure ◽  
Microstructure And Mechanical Properties ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
Rapid Heat Treatment

In this paper Ti2AlC/TiAl composites were in-situ fabricated by spark plasma sintering (SPS) and then the effects of rapid heat-treatment on microstructure and mechanical properties of Ti2AlC/TiAl composites were investigated. After rapid heat-treatment the microstructure of TiAl matrix was significantly transformed from the near γ microstructure to duplex microstructure. Ti2AlC particles effectively refined the γ phase grains and the α2/γ lamellar colony microstructure. For the Ti2AlC/TiAl composite after rapid heat-treatment at 1200°C, the bending strength and fracture toughness reached 956.8MPa and 22.8MPa·m1/2, respectively.