Optimization of hot-press conditions of Zn4Sb3 for high thermoelectric performance. II. Mechanical properties

2005 ◽  
Vol 388 (1) ◽  
pp. 118-121 ◽  
Author(s):  
K. Ueno ◽  
A. Yamamoto ◽  
T. Noguchi ◽  
T. Inoue ◽  
S. Sodeoka ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermoelectric Performance ◽  
Hot Press

Optimization of Hot-Press Conditions of Zn4Sb3 for High Thermoelectric Performance. Part 2. Mechanical Properties.

ChemInform ◽  
2005 ◽  
Vol 36 (17) ◽  
Author(s):  
K. Ueno ◽  
A. Yamamoto ◽  
T. Noguchi ◽  
T. Inoue ◽  
S. Sodeoka ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermoelectric Performance ◽  
Hot Press

scholarly journals Effect of Sintering Temperature on Microstructure and Mechanical Properties of Hot-Pressed Fe/FeAl2O4 Composite

Crystals ◽  
2021 ◽  
Vol 11 (4) ◽  
pp. 422
Author(s):  
Kuai Zhang ◽  
Yungang Li ◽  
Hongyan Yan ◽  
Chuang Wang ◽  
Hui Li ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Bending Strength ◽  
Sintering Temperature ◽  
Raw Materials ◽  
Hot Press ◽  
Microstructure And Mechanical Properties ◽  
Powder Particles ◽  
Hot Press Sintering ◽  
Sintering Method

An Fe/FeAl2O4 composite was prepared with Fe-Fe2O3-Al2O3 powder by a hot press sintering method. The mass ratio was 6:1:2, sintering pressure was 30 MPa, and holding time was 120 min. The raw materials for the powder particles were respectively 1 µm (Fe), 0.5 µm (Fe2O3), and 1 µm (Al2O3) in diameter. The effect of sintering temperature on the microstructure and mechanical properties of Fe/FeAl2O4 composite was studied. The results showed that Fe/FeAl2O4 composite was formed by in situ reaction at 1300 °C–1500 °C. With the increased sintering temperature, the microstructure and mechanical properties of the Fe/FeAl2O4 composite showed a change law that initially became better and then became worse. The best microstructure and optimal mechanical properties were obtained at 1400 °C. At this temperature, the grain size of Fe and FeAl2O4 phases in Fe/FeAl2O4 composite was uniform, the relative density was 96.7%, and the Vickers hardness and bending strength were 1.88 GPa and 280.0 MPa, respectively. The wettability between Fe and FeAl2O4 was enhanced with increased sintering temperature. And then the densification process was accelerated. Finally, the microstructure and mechanical properties of the Fe/FeAl2O4 composite were improved.

Experimental study on mechanical properties of polypropylene nanocomposites reinforced with a hybrid graphene/PP-g-MA/kenaf fiber by response surface methodology

2021 ◽  
pp. 009524432110153
Author(s):  
Jaber Mirzaei ◽  
Abdolhossein Fereidoon ◽  
Ahmad Ghasemi-Ghalebahman
Keyword(s):  
Mechanical Properties ◽  
Response Surface Methodology ◽  
Elastic Modulus ◽  
Response Surface ◽  
Graphene Nanosheets ◽  
Hot Press ◽  
Kenaf Fiber ◽  
Polypropylene Nanocomposites ◽  
Kenaf Fibers ◽  
Internal Mixer

In this study, the mechanical properties of polypropylene (PP)-based nanocomposites reinforced with graphene nanosheets, kenaf fiber, and polypropylene-grafted maleic anhydride (PP-g-MA) were investigated. Response surface methodology (RSM) based on Box–Behnken design (BBD) was used as the experimental design. The blends fabricated in three levels of parameters include 0, 0.75, and 1.5 wt% graphene nanosheets, 0, 7.5, and 15 wt% kenaf fiber, and 0, 3, and 6 wt% PP-g-MA, prepared by an internal mixer and a hot press machine. The fiber length was 5 mm and was being constant for all samples. Tensile, flexural, and impact tests were conducted to determine the blend properties. The purpose of this research is to achieve the highest mechanical properties of the considered nanocomposite blend. The addition of graphene nanosheets to 1 wt% increased the tensile, flexural, and impact strengths by 16%, 24%, and 19%, respectively, and an addition up to 1.5 wt% reduced them. With further addition of graphene nanosheets until 1.5 wt%, the elastic modulus was increased by 70%. Adding the kenaf fiber up to 15 wt% increased the elastic modulus, tensile, flexural, and impact strength by 24%, 84%, 18%, and 11%, respectively. The addition of PP-g-MA has increased the adhesion, dispersion and compatibility of graphene nanosheets and kenaf fibers with matrix. With 6 wt% PP-g-MA, the tensile strength and elastic modulus were increased by 18% and 75%, respectively. The addition of PP-g-MA to 5 wt% increased the flexural and impact strengths by 10% and 5%, respectively. From the entire experimental data, the optimum values for elastic modulus, as well as, tensile, flexural, and impact strengths in the blends were obtained to be 4 GPa, 33.7896 MPa, 57.6306 MPa, and 100.1421 J/m, respectively. Finally, samples were studied by FE-SEM to check the dispersion of graphene nanosheets, PP-g-MA and kenaf fibers in the polymeric matrix.

Experimental Assessment of High Temperature Formability of Boron Steel Sheet Manufactured With a Spring Compound Bending Die

2012 ◽  
Vol 134 (2) ◽  
Author(s):  
Yang Li ◽  
Yong-Phil Jeon ◽  
Chung-Gil Kang
Keyword(s):  
Mechanical Properties ◽  
Heating Temperature ◽  
Boron Steel ◽  
Hot Press ◽  
Forming Process ◽  
Steel Sheets ◽  
Press Forming ◽  
Bending Process ◽  
Tension Testing ◽  
Hot Press Forming

Bending behavior occurs in the hot press forming process, resulting in many cases of failure during forming. To address the problem of cracking and improve the formability and mechanical properties of boron steel sheets in the bending process, an experiment has been carried out by using a spring compound bending die. Also, a comparison has been made between the traditional U-bending die and the spring compound bending die with regard to formability. The influence of the parameters for hot press forming such as the heating temperature, punch speed, and die radii on the mechanical properties and microstructure was analyzed by tension testing and metallographic observations.

Effects of MgO and Y2O3 on the Microstructure and Mechanical Properties of Al2O3 Ceramics

2013 ◽  
Vol 589-590 ◽  
pp. 572-577 ◽  
Author(s):  
Hua He Liu ◽  
Han Lian Liu ◽  
Chuan Zhen Huang ◽  
Bin Zou ◽  
Ya Cong Chai
Keyword(s):  
Mechanical Properties ◽  
Sintering Temperature ◽  
Hot Press ◽  
Composite Ceramics ◽  
Microstructure And Mechanical Properties ◽  
Suitable Amount ◽  
Hot Press Sintering ◽  
Grains Refinement ◽  
Better Than

Al2O3-MgO, Al2O3-Y2O3 and Al2O3-MgO-Y2O3 composite ceramics were fabricated respectively by hot-press sintering technique. With the analysis of the mechanical properties and microstructure, it was found that single additive MgO could be more favorable to the grains’ refinement and densification than Y2O3; the composite additive including both MgO and Y2O3 was better than single additive MgO or Y2O3, because their interactions could improve the mechanical properties of the Al2O3 ceramics; The sintering temperature could be reduced by adding the suitable amount of composite additives.

Effects of TiN Content on Mechanical Properties and Microstructure of ATN Materials

2013 ◽  
Vol 589-590 ◽  
pp. 590-593 ◽  
Author(s):  
Min Wang ◽  
Jun Zhao
Keyword(s):  
Mechanical Properties ◽  
Mechanical Property ◽  
Fracture Toughness ◽  
Vickers Hardness ◽  
Bending Strength ◽  
Sintering Temperature ◽  
Ceramic Materials ◽  
Hot Press ◽  
Hot Press Sintering ◽  
Tin Content

In order to investigate the effects of TiN content on Al2O3/TiN ceramic material (ATN), the ATN ceramic materials were prepared of TiN content in 30%, 40%, 50%, 60% in the condition of hot press sintering. The sintering temperature is 1700°C, the sintering press is 32MPa, and the holding time are 5min, 10min, 15min. The effects of TiN content on mechanical properties and microstructure of ATN ceramic materials were investigated by analyzing the bending strength, hardness, fracture toughness. The results show that ATN50 has the best mechanical property, its bending strength is 659.41MPa, vickers hardness is 13.79GPa, fracture toughness is 7.06MPa·m1/2. It is indicated that the TiN content has important effect on microstructure and mechanical properties of ATN ceramic materials.

analysis of mechanical properties of ceiling boards based on corn cobs and coconut coir waste with latex adhesive

2021 ◽  
Vol 5 (2) ◽  
pp. 1
Author(s):  
Ety Jumiati ◽  
Ufik Eliati Tumanggor ◽  
Abdul Halim Daulay
Keyword(s):  
Mechanical Properties ◽  
Flexural Strength ◽  
Fracture Strength ◽  
Test Results ◽  
Hot Press ◽  
Optimal Result ◽  
Corn Cob ◽  
Corn Cobs ◽  
Test Parameters ◽  
Coconut Coir

<p align="center"><strong><em>Abstract</em></strong></p><p>Ceiling evelopment by utilizing waste corn cobs, coconut coir with gypsum flour an the adition of latex adhesive. Variations in the composition of the mixture of corn cobs, coconut coir, gypsum flour with latex adhesive include sample A (0:0:100:15), sample B (3:3:94:15), sample C (6:6:88:15), sample D (9:9:82:15), sample E (12:12:76:15), and sample F (15:15:70:15) with emphasis using a <em>hot press </em>and drying for 28 days. The test parameters include flexural strength and fracture strength. The test results show that sample B in the composition (3:3:94:15) is the optimal result. In this composition, the resulting ceiling board has the characteristics of a flexural strength of 3966,39 kgf/cm<sup>2</sup> and a fracture strength of 1088,6 kgf/cm<sup>2</sup>.</p><p><strong><em>Keyword :</em></strong><em> Lateks , Ceiling Board, Coconut Coir, Corn Cob</em></p><p><em> </em></p>

Mechanical Properties and Thermal Stability of the High-Thermoelectric-Performance Cu2Se Compound

2021 ◽  
Vol 13 (38) ◽  
pp. 45736-45743
Author(s):  
Jian Zhang ◽  
Cheng Zhang ◽  
Ting Zhu ◽  
Yonggao Yan ◽  
Xianli Su ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Thermoelectric Performance ◽  
Thermal Stability Of
Sign in / Sign up

Export Citation Format

Share Document