Microstructure and room temperature fracture toughness of directionally solidified NiAl–Mo eutectic in situ composites

2012 ◽  
Vol 21 (1) ◽  
pp. 18-25 ◽  
Author(s):  
Jian-Fei Zhang ◽  
Jun Shen ◽  
Zhao Shang ◽  
Zhou-Rong Feng ◽  
Ling-Shui Wang ◽  
...  
Keyword(s):  
Fracture Toughness ◽  
Room Temperature ◽  
Directionally Solidified ◽  
In Situ Composites ◽  
Temperature Fracture

Microstructure and room temperature fracture toughness of Nbss/Nb5Si3 in situ composites

2001 ◽  
Vol 9 (9) ◽  
pp. 827-834 ◽  
Author(s):  
Won-Yong Kim ◽  
Hisao Tanaka ◽  
Akio Kasama ◽  
Shuji Hanada
Keyword(s):  
Fracture Toughness ◽  
Room Temperature ◽  
In Situ Composites ◽  
Temperature Fracture

Microstructures and Properties of Ds in-Situ Composites of Nb-Ti-Si Alloys

1994 ◽  
Vol 364 ◽  
Author(s):  
B. P. Bewlay ◽  
M. R. Jackson ◽  
W. J. Reeder ◽  
H. A. Lipsitt
Keyword(s):  
Mechanical Properties ◽  
Solid Solution ◽  
Fracture Toughness ◽  
Room Temperature ◽  
In Situ Composites ◽  
Environmental Resistance ◽  
High Temperature Mechanical Properties ◽  
Three Phase ◽  
Temperature Fracture

AbstractIn-situ composites based on binary Nb-Si alloys and consisting of a Nb solid solution with Nb3Si or Nb5Si3 have shown a promising combination of low temperature and high temperature mechanical properties. The environmental resistance and room temperature fracture toughness of these composites can be further enhanced by additions such as Ti, Hf, Cr, and Al. In the present study, ternary Nb-Ti-Si alloys were prepared by directional solidification to generate aligned two and three phase composites containing a Nb solid solution with Nb3Si and/or Nb5Si3. The present paper will describe microstructures, phase equilibria and fracture toughness of these composites. The improvement in the room temperature fracture toughness over binary Nb-Nb5Si3 composites is discussed.

Effects of Re Alloying on Mechanical Properties of In-Situ Composites with Base Composition of Nb-18Si-2HfC

2006 ◽  
Vol 306-308 ◽  
pp. 941-946
Author(s):  
Sheng Wu Wang ◽  
Tatsuo Tabaru ◽  
Hisatoshi Hirai ◽  
Hideto Ueno
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
High Temperature ◽  
Base Composition ◽  
Room Temperature ◽  
High Temperature Strength ◽  
Strengthening Effect ◽  
In Situ Composites ◽  
Temperature Fracture

Nb-base in-situ composites with the base composition of Nb-18Si-2HfC were prepared by conventional arc-melting. Their microstructures and mechanical properties, such as high-temperature strength and room temperature fracture toughness, were investigated to elucidate the effects of Re alloying. The in-situ composites predominantly have eutectic microstructures consisting of an Nb solid solution (NbSS) and Nb5Si3. The compressive strength increased with the increasing Re contents at 1470K and not at 1670 K. The strengthening effect observed at 1470 K is higher than that by W and Mo. Re alloying of about 2 % is valuable for improving both the high temperature strength and room temperature fracture toughness of Nb-18Si-2HfC base materials.

Mechanical properties of NiAl-Mo composites produced by specially controlled directional solidification

2012 ◽  
Vol 1516 ◽  
pp. 255-260 ◽  
Author(s):  
G. Zhang ◽  
L. Hu ◽  
W. Hu ◽  
G. Gottstein ◽  
S. Bogner ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Directional Solidification ◽  
Creep Resistance ◽  
Room Temperature ◽  
Growth Direction ◽  
Nominal Composition ◽  
Potential Candidate ◽  
In Situ Composites

ABSTRACTMo fiber reinforced NiAl in-situ composites with a nominal composition Ni-43.8Al-9.5Mo (at.%) were produced by specially controlled directional solidification (DS) using a laboratory-scale Bridgman furnace equipped with a liquid metal cooling (LMC) device. In these composites, single crystalline Mo fibers were precipitated out through eutectic reaction and aligned parallel to the growth direction of the ingot. Mechanical properties, i.e. the creep resistance at high temperatures (HT, between 900 °C and 1200 °C) and the fracture toughness at room temperature (RT) of in-situ NiAl-Mo composites, were characterized by tensile creep (along the growth direction) and flexure (four-point bending, vertical to the growth direction) tests, respectively. In the current study, a steady creep rate of 10-6s-1 at 1100 °C under an initial applied tensile stress of 150MPa was measured. The flexure tests sustained a fracture toughness of 14.5 MPa·m1/2at room temperature. Compared to binary NiAl and other NiAl alloys, these properties showed a remarkably improvement in creep resistance at HT and fracture toughness at RT that makes this composite a potential candidate material for structural application at the temperatures above 1000 °C. The mechanisms responsible for the improvement of the mechanical properties in NiAl-Mo in-situ composites were discussed based on the investigation results.

Processing and Mechanical Properties of RuAl-Based Alloys

2007 ◽  
Vol 539-543 ◽  
pp. 1469-1474 ◽  
Author(s):  
T.D. Reynolds ◽  
M. Acosta ◽  
David R. Johnson
Keyword(s):  
Fracture Toughness ◽  
Cyclic Oxidation ◽  
Room Temperature ◽  
Single Phase ◽  
Tensile Ductility ◽  
Tensile Behavior ◽  
Directionally Solidified ◽  
Two Phase ◽  
Heat Treated ◽  
Temperature Fracture

Alloys of Ru-Al-Cr with compositions between Ru-10Al-35Cr and Ru-3Al-39Cr (at.%) were directionally solidified and heat treated to produce single phase hcp-Ru(Cr,Al) and two phase B2-hcp microstructures. The room temperature fracture toughness, tensile behavior, and cyclic oxidation behavior at 1100°C were investigated and compared to previous results measured from RuAl and Ru-Al-Mo alloys. For microstructures consisting of a Ru(Cr,Al) matrix with fine RuAl precipitate, a good room temperature fracture toughness, tensile ductility, and oxidation resistance at 1100°C were measured.

Ti-Modified Niobium-Silicide Based Directionally Solidified in-situ Composites

1996 ◽  
Vol 460 ◽  
Author(s):  
B. P. Bewlay ◽  
M. R. Jackson ◽  
H. A. Lipsitt
Keyword(s):  
Solid Solution ◽  
Fracture Toughness ◽  
High Temperature ◽  
Cold Crucible ◽  
Directionally Solidified ◽  
In Situ Composites ◽  
Czochralski Crystal Growth ◽  
Three Phase ◽  
Binary Eutectic

ABSTRACTThis paper examines microstructure-property relationships in high-temperature directionally solidified (DS) in-situ composites based on Nb silicides, such as Nb3Si and Nb5Si3. These in-situ composites are based on the Nb3Si-Nb binary eutectic, and are alloyed with Ti. They were prepared using cold crucible Czochralski crystal growth. Ternary Nb-Ti-Si alloys with Ti concentrations from 9 to 45%, and Si concentrations from 10 to 25%, were directionally solidified to generate aligned two- and three-phase composites containing a Nb solid solution with Nb3Si and Nb5Si3 silicides. Fracture toughness values generally greater than 10 MPa√m were measured in these composites. For a given Si concentration, the fracture toughness of the Ti-containing composites was increased ∼ 6 MPa√m over that of the binary alloy composites. The effects of Si concentration, and a range of Nb:Ti ratios, on microstructure, phase equilibria, and fracture toughness were examined.