Development of adiabatic shear bands in annealed 316L stainless steel: Part II. TEM studies of the evolution of microstructure during deformation localization

2006 ◽  
Vol 37 (8) ◽  
pp. 2447-2458 ◽  
Author(s):  
Q. Xue ◽  
G. T. Gray
Keyword(s):  
Stainless Steel ◽  
316L Stainless Steel ◽  
Shear Bands ◽  
Steel Part ◽  
Adiabatic Shear ◽  
Adiabatic Shear Bands ◽  
Deformation Localization ◽  
Stainless Steel Part ◽  
Evolution Of Microstructure

The Effect of Sigma Phase vs Chromium Carbides On the Intergranular Corrosion Of Type 316 and 316L Stainless Steel (Part 2—Laboratory Investigation)★

CORROSION ◽  
1959 ◽  
Vol 15 (5) ◽  
pp. 17-28 ◽  
Author(s):  
DONALD WARREN
Keyword(s):  
Stainless Steel ◽  
Intergranular Corrosion ◽  
Sigma Phase ◽  
316L Stainless Steel ◽  
Steel Part ◽  
Intergranular Attack ◽  
Acid Media ◽  
Chromium Carbides ◽  
Type 316L ◽  
Stainless Steel Part

Abstract A laboratory study was made of the intergranular corrosion behavior of Types 316 and 316L stainless steel in 14 different acid environments. Included were nitric, nitric-hydrofluoric, acetic, citric, sulfuric, lactic, oxalic, formic and phosphoric acids. Results of this study showed that sensitized or welded Type 316L had excellent resistance to intergranular attack in all of the acid media except nitric. This was true despite the presence of a continuous network of sigma phase in the grain boundaries of the sensitized steel. In contrast, Type 316 having a continuous grain boundary network of chromium carbides underwent severe intergranular corrosion in 12 of the 14 environments studied. 3.2.2

scholarly journals Influence of H2O on localised corrosion of 316L stainless steel Part 1: coupon testing

2021 ◽  
Author(s):  
J Hesketh ◽  
E J F Dickinson ◽  
G McMahon ◽  
M Martin ◽  
A Turnbull ◽  
...  
Keyword(s):  
Stainless Steel ◽  
316L Stainless Steel ◽  
Steel Part ◽  
Stainless Steel Part
Sign in / Sign up

Export Citation Format

Share Document