Energy saving technology for sintering of black bricks from high-siliceous clay

MRS Advances ◽  
2020 ◽  
Vol 5 (61) ◽  
pp. 3123-3131
Author(s):  
Mario Flores Nicolas ◽  
Marina Vlasova ◽  
Pedro Antonio Márquez Aguilar ◽  
Mykola Kakazey ◽  
Marcos Mauricio Chávez Cano ◽  
...  
Keyword(s):  
Low Temperature ◽  
Oxygen Deficiency ◽  
Glass Ceramics ◽  
Total Content ◽  
Ceramic Materials ◽  
Ternary Mixtures ◽  
High Porosity ◽  
Reducing Conditions ◽  
Binary And Ternary Mixtures ◽  
Dark Color

AbstractThe low-temperature synthesis of bricks prepared from high-siliceous clays by the method of plastic molding of blanks was used. For the preparation of brick blanks, binary and ternary mixtures of high-siliceous clays, black sand, and bottle glass cullet were used. Gray-black low-porosity and high-porosity ceramics was obtained by sintering under conditions of oxygen deficiency. It has been established that to initiate plastic in mixtures containing high-siliceous clay, it is necessary to add montmorillonite/bentonite additives, carry out low-temperature sintering, and introduce low-melting glass additives with a melting point ranging from 750 to 800 °C. The performed investigations have shown that the sintering of mixtures with a total content of iron oxide of about 5 wt% under reducing conditions at Tsint. = 800°C for 8 h leads to the formation of glass ceramics consisting of quartz, feldspars, and a phase. The main sources of the appearance of a dark color is the formation of [Fe3+O4]4- and [Fe3+O6]9- anions in the composition of the glass phase and feldspars. By changing the contents of clay, sand, and glass in sintering, it is possible to obtain two types of ceramic materials: (a) in the form of building bricks and (b) in the form of porous fillers.