Post‐cracking behavior of polypropylene fiber reinforced concrete under bending and uniaxial tensile tests

2019 ◽  
Vol 20 (4) ◽  
pp. 1411-1424 ◽  
Author(s):  
Antonio Mudadu ◽  
Giuseppe Tiberti ◽  
Giovanni A. Plizzari ◽  
Alessandro Morbi
Keyword(s):  
Reinforced Concrete ◽  
Polypropylene Fiber ◽  
Tensile Tests ◽  
Fiber Reinforced Concrete ◽  
Uniaxial Tensile ◽  
Fiber Reinforced ◽  
Cracking Behavior ◽  
Polypropylene Fiber Reinforced Concrete

scholarly journals Tension Stiffening Behavior of Polypropylene Fiber- Reinforced Concrete Tension Members

2021 ◽  
Vol 53 (2) ◽  
pp. 210209
Author(s):  
Aris Aryanto ◽  
Berto Juergen Winata
Keyword(s):  
Reinforced Concrete ◽  
Polypropylene Fiber ◽  
Fiber Reinforced Concrete ◽  
Polypropylene Fibers ◽  
Fiber Reinforced ◽  
Tension Stiffening ◽  
Cracking Behavior ◽  
Tension Members ◽  
Polypropylene Fiber Reinforced Concrete ◽  
Fiber Addition

This paper focuses on comparing the behavior of RC tension members with and without the addition of polypropylene fibers at various corrosion levels. Eight cylindrical tensile specimens were tested to evaluate their tension-stiffening and cracking behavior. The content of polypropylene fiber added into the concrete mix was the main variable (0.25%, 0.50%, 0.75%, and 1.0% of total volume). The corrosion level was varied from slight (5%), medium (10%) to severe (30%) and, like the other variables, applied only to 1.0% polypropylene fiber-reinforced concrete (PFRC) specimens. The test results showed that the fiber addition significantly increased the tension-stiffening effect but was largely unable to reduce the effect of bond degradation caused by corrosion. Moreover, the addition of polypropylene fibers was able to improve the cracking behavior in terms of crack propagation, as shown by smaller crack spacing compared to the specimen without fiber addition at the same corrosion level.

Improved Early-Age Cohesive Stress Response from Hybrid Blends of Micro and Macro Fibers

2021 ◽  
Vol 1046 ◽  
pp. 1-7
Author(s):  
Manjunath V. Bhogone ◽  
Kolluru V.L. Subramaniam
Keyword(s):  
Reinforced Concrete ◽  
Stress Response ◽  
Volume Fraction ◽  
Polypropylene Fiber ◽  
Fiber Reinforced Concrete ◽  
Early Age ◽  
Fiber Reinforced ◽  
Cohesive Stress ◽  
Concrete Matrix ◽  
Polypropylene Fiber Reinforced Concrete

The fracture response of macro polypropylene fiber reinforced concrete (PPFRC) and hybrid blend of macro and micro polypropylene fiber reinforced concrete (HyFRC) are evaluated at 1, 3, 7 and 28 days. There is an improvement in the early-age fracture response of HyFRC compared to PPFRC. The changing cohesive stress-crack separation relationship produced by ageing of the concrete matrix is determined from the fracture test responses. An improved early-age cohesive stress response is obtained from the hybrid blend containing micro and macro fibers. The hybrid fiber blend also has a higher tensile strength at early age when compared to an identical volume fraction of macro polypropylene fibers.

Sign in / Sign up

Export Citation Format

Share Document