Flexible solid-state supercapacitor of metal-organic framework coated on carbon nanotube film interconnected by electrochemically -codeposited PEDOT-GO

2016 ◽  
Vol 1 (2) ◽  
pp. 285-289 ◽  
Author(s):  
Dongying Fu ◽  
Haihan Zhou ◽  
Xian-Ming Zhang ◽  
Gaoyi Han ◽  
Yunzhen Chang ◽  
...  
Keyword(s):  
Carbon Nanotube ◽  
Solid State ◽  
Metal Organic Framework ◽  
Carbon Nanotube Film ◽  
Metal Organic ◽  
Organic Framework

scholarly journals HKUST-1@IL-Li Solid-state Electrolyte with 3D Ionic Channels and Enhanced Fast Li+ Transport for Lithium Metal Batteries at High Temperature

Nanomaterials ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 736
Author(s):  
Man Li ◽  
Tao Chen ◽  
Seunghyun Song ◽  
Yang Li ◽  
Joonho Bae
Keyword(s):  
High Temperature ◽  
Solid State ◽  
Solid Electrolyte ◽  
Metal Organic Framework ◽  
Ionic Channels ◽  
Transference Numbers ◽  
Lithium Metal ◽  
Lithium Metal Batteries ◽  
Metal Organic ◽  
Organic Framework

The challenge of safety problems in lithium batteries caused by conventional electrolytes at high temperatures is addressed in this study. A novel solid electrolyte (HKUST-1@IL-Li) was fabricated by immobilizing ionic liquid ([EMIM][TFSI]) in the nanopores of a HKUST-1 metal–organic framework. 3D angstrom-level ionic channels of the metal–organic framework (MOF) host were used to restrict electrolyte anions and acted as “highways” for fast Li+ transport. In addition, lower interfacial resistance between HKUST-1@IL-Li and electrodes was achieved by a wetted contact through open tunnels at the atomic scale. Excellent high thermal stability up to 300 °C and electrochemical properties are observed, including ionic conductivities and Li+ transference numbers of 0.68 × 10-4 S·cm-1 and 0.46, respectively, at 25 °C, and 6.85 × 10-4 S·cm-1 and 0.68, respectively, at 100 °C. A stable Li metal plating/stripping process was observed at 100 °C, suggesting an effectively suppressed growth of Li dendrites. The as-fabricated LiFePO4/HKUST-1@IL-Li/Li solid-state battery exhibits remarkable performance at high temperature with an initial discharge capacity of 144 mAh g-1 at 0.5 C and a high capacity retention of 92% after 100 cycles. Thus, the solid electrolyte in this study demonstrates promising applicability in lithium metal batteries with high performance under extreme thermal environmental conditions.

Li-based MOF-derived multifunctional PEO polymer solid-state electrolyte for lithium energy storage

2022 ◽  
Author(s):  
Xiang Han ◽  
Tiantian Wu ◽  
Lanhui Gu ◽  
Dian Tian
Keyword(s):  
Energy Storage ◽  
Solid State ◽  
Metal Organic Framework ◽  
Three Dimensional ◽  
Isophthalic Acid ◽  
Solid State Electrolyte ◽  
Metal Organic ◽  
Solvothermal Conditions ◽  
Organic Framework

A three-dimensional (3D) metal-organic framework containing Li-oxygen clusters, namely {[Li2(IPA)]·DMF}n (1) (H2IPA = isophthalic acid), has been constructed under solvothermal conditions. The Li-based MOF can be applied to lithium energy...

Sign in / Sign up

Export Citation Format

Share Document