Fatigue crack propagation mechanisms in poly(methyl methacrylate) byin situ observation with a scanning laser microscope

2001 ◽  
Vol 39 (24) ◽  
pp. 3103-3113 ◽  
Author(s):  
C. Ishiyama ◽  
T. Asai ◽  
M. Kobayashi ◽  
M. Shimojo ◽  
Y. Higo
Keyword(s):  
Fatigue Crack ◽  
Crack Propagation ◽  
Methyl Methacrylate ◽  
Fatigue Crack Propagation ◽  
Scanning Laser ◽  
Poly Methyl Methacrylate

Craze development in poly(methyl methacrylate) during stable fatigue crack propagation

1984 ◽  
Vol 24 (10) ◽  
pp. 833-842 ◽  
Author(s):  
R. W. Lang ◽  
J. A. Manson ◽  
R. W. Hertzberg ◽  
R. Schirrer
Keyword(s):  
Fatigue Crack ◽  
Crack Propagation ◽  
Methyl Methacrylate ◽  
Fatigue Crack Propagation ◽  
Poly Methyl Methacrylate

High Cycle Fatigue and Fatigue Crack Propagation Behaviors of Modified A7075-T73 Alloy

2014 ◽  
Vol 52 (4) ◽  
pp. 283-291 ◽  
Author(s):  
Gwan Yeong Kim ◽  
Kyu Sik Kim ◽  
Joong Cheol Park ◽  
Shae Kwang Kim ◽  
Young Ok Yoon ◽  
...  
Keyword(s):  
Fatigue Crack ◽  
Crack Propagation ◽  
Fatigue Crack Propagation ◽  
High Cycle Fatigue ◽  
Cycle Fatigue

scholarly journals Structure, processing and performance of ultra-high molecular weight polyethylene (IUPAC Technical Report). Part 4: sporadic fatigue crack propagation

2020 ◽  
Vol 92 (9) ◽  
pp. 1521-1536
Author(s):  
Clive Bucknall ◽  
Volker Altstädt ◽  
Dietmar Auhl ◽  
Paul Buckley ◽  
Dirk Dijkstra ◽  
...  
Keyword(s):  
Molecular Weight ◽  
Fatigue Crack ◽  
Crack Propagation ◽  
High Molecular Weight ◽  
Fatigue Crack Propagation ◽  
Crack Tip ◽  
Individual Growth ◽  
Paris Equation ◽  
Number Of Cycles ◽  
Ultra High Molecular Weight

AbstractFatigue tests were carried out on compression mouldings supplied by a leading polymer manufacturer. They were made from three batches of ultra-high molecular weight polyethylene (UHMWPE) with weight-average relative molar masses, ${\overline{M}}_{\mathrm{W}}$, of about 0.6 × 106, 5 × 106 and 9 × 106. In 10 mm thick compact tension specimens, crack propagation was so erratic that it was impossible to follow standard procedure, where crack-tip stress intensity amplitude, ΔK, is raised incrementally, and the resulting crack propagation rate, da/dN, increases, following the Paris equation, where a is crack length and N is number of cycles. Instead, most of the tests were conducted at fixed high values of ΔK. Typically, da/dN then started at a high level, but decreased irregularly during the test. Micrographs of fracture surfaces showed that crack propagation was sporadic in these specimens. In one test, at ΔK = 2.3 MPa m0.5, there were crack-arrest marks at intervals Δa of about 2 μm, while the number of cycles between individual growth steps increased from 1 to more than 1000 and the fracture surface showed increasing evidence of plastic deformation. It is concluded that sporadic crack propagation was caused by energy-dissipating crazing, which was initiated close to the crack tip under plane strain conditions in mouldings that were not fully consolidated. By contrast, fatigue crack propagation in 4 mm thick specimens followed the Paris equation approximately. The results from all four reports on this project are reviewed, and the possibility of using fatigue testing as a quality assurance procedure for melt-processed UHMWPE is discussed.