Environmental stress cracking of poly(acrylonitrile-butadiene-styrene)

1999 ◽  
Vol 39 (2) ◽  
pp. 268-273 ◽  
Author(s):  
Takafumi Kawaguchi ◽  
Hiroyuki Nishimura ◽  
Fumiaki Miwa ◽  
Kazuhiro Abe ◽  
Takashi Kuriyama ◽  
...  
Keyword(s):  
Environmental Stress ◽  
Acrylonitrile Butadiene Styrene ◽  
Stress Cracking ◽  
Environmental Stress Cracking ◽  
Poly Acrylonitrile ◽  
Butadiene Styrene

scholarly journals Difference in polypropylene fragmentation mechanism between marine and terrestrial regions

2021 ◽  
Vol 3 (9) ◽  
Author(s):  
Hisayuki Nakatani ◽  
Takuya Muraoka ◽  
Yuina Ohshima ◽  
Suguru Motokucho
Keyword(s):  
Environmental Stress ◽  
Advanced Oxidation Process ◽  
List Type ◽  
Patch Structure ◽  
Stress Cracking ◽  
Fragmentation Mechanisms ◽  
Environmental Stress Cracking ◽  
Speed Up ◽  
Degradation Time ◽  
Delamination Behavior

AbstractTwo kinds of marine polypropylene (M1-PP and M2-PP) and one land PP (L-PP) samples were collected from two beaches and land in Japan, respectively, to study the fragmentation mechanisms. Delamination was observed on both M1-PP and M2-PP surfaces. Moreover, there was no delamination but an abrasion patch structure on the surface of L-PP. The delamination was studied using an advanced oxidation process-degraded PP as the marine PP model. The number and shape of cracks varied with an increase in degradation time. The fluctuations in the values and ratios of the carbonyl index as well as the weight change ratio were due to repeated oxidation and delamination. We found that the delamination behavior depends on the oxidation state. Poly(oxyethylene)8 octylphenyl ether (POE8) surfactant treatment caused the delamination to speed up, which is a typical characteristic of polyolefin environmental stress cracking (ESC). These results reveal that delamination is based on ESC.Article Highlights Two kinds of marine and one land polypropylene (PP) samples were collected from two beaches and land, respectively, to study the fragmentation mechanisms. Delamination was observed on both of marine PP surfaces. Moreover, there was no delamination but an abrasion patch structure on the land PP surface. We found that the delamination was based on environmental stress cracking mechanism by employing a marine PP model.