Mode I and Mode II interlaminar fracture behavior of E-glass fiber reinforced epoxy composites modified with reduced exfoliated graphite oxide

2018 ◽  
Vol 39 (S4) ◽  
pp. E2506-E2518 ◽  
Author(s):  
Lokasani Bhanuprakash ◽  
Abins Ali ◽  
Rashad Mokkoth ◽  
Soney Varghese
Keyword(s):  
Glass Fiber ◽  
Graphite Oxide ◽  
Fracture Behavior ◽  
Exfoliated Graphite ◽  
Epoxy Composites ◽  
Mode I ◽  
Mode Ii ◽  
Fiber Reinforced ◽  
Interlaminar Fracture ◽  
Glass Fiber Reinforced

scholarly journals Woven Glass Fiber Composites with Aligned Carbon Nanotube Sheet Interlayers

2016 ◽  
Vol 2016 ◽  
pp. 1-9 ◽  
Author(s):  
Hardik Bhanushali ◽  
Philip D. Bradford
Keyword(s):  
Fracture Toughness ◽  
Glass Fiber ◽  
Mode I ◽  
Mode Ii ◽  
Interlaminar Fracture Toughness ◽  
Fiber Reinforced ◽  
Interlaminar Fracture ◽  
Glass Fiber Reinforced ◽  
Short Beam ◽  
Woven Glass Fiber

This investigation describes the design, fabrication, and testing of woven glass fiber reinforced epoxy matrix laminates with aligned CNT sheets integrated between plies in order to improve the matrix dominated through thickness properties such as the interlaminar fracture toughness at ply interfaces. Using aligned CNT sheets allows for a concentration of millimeter long CNTs at the most likely point of laminate failure. Mode I and Mode II interlaminar fracture toughness of various CNT modified samples were investigated using double cantilever beam (DCB) and end notched flexure (ENF) experiments, respectively. Short beam strength (SBS) and in-plane tensile properties of the CNT modified samples were also investigated. Moderate improvement was observed in Mode I and Mode II fracture toughness at crack initiation when aligned CNT sheets with a basis weight of 0.354 g/m2were used to modify the ply interface. No compromise in the in-plane mechanical properties of the laminate was observed and very little improvement was observed in the shear related short beam strength of the CNT modified laminates as compared to the control samples. Integration of aligned CNT sheets into the composite laminate imparted in-plane and through thickness electrical properties into the nonconductive glass fiber reinforced epoxy composite laminates.

scholarly journals Effect of sewage sludge ash filler on mode I and mode II interlaminar fracture toughness of S-glass/epoxy composites

2018 ◽  
Vol 1 (2) ◽  
Author(s):  
Mohamad Alsaadi 1,2 ◽  
Ahmet Erkliğ 2
Keyword(s):  
Fracture Toughness ◽  
Sewage Sludge ◽  
Epoxy Composites ◽  
Mode I ◽  
Mode Ii ◽  
Interlaminar Fracture Toughness ◽  
Sewage Sludge Ash ◽  
Interlaminar Fracture ◽  
Glass Fiber Reinforced ◽  
Sludge Ash

In this study, the influence of sewage sludge ash (SSA) waste particle contents on the mechanical properties and interlaminar fracture toughness for mode I and mode II delamination of S-glass fiber reinforced epoxy composites were investigated. Composite laminate specimens for tensile, flexural double-cantilever beam (DCB) and end-notched flexure (ENF) tests were prepared and tested according to ASTM standards with 5, 10, 15 and 20 wt% SSA filled S-glass/epoxy composites. Properties improvement reasons was explained based on optical and scanning electron microscopy. The highest improvement in tensile and flexural strength was obtained with 10 wt% content of SSA. The highest mode I and mode II interlaminar fracture toughness’s were obtained with 15 wt% content of SSA. The mode I and mode II interlaminar fracture toughness’s improved by 33 and 63.6%, respectively, compared to the composite without SSA.