Corrosion resistance evaluation of Ni-P\nano-ZrO2 composite coatings by electrochemical impedance spectroscopy and machine vision method

2014 ◽  
Vol 66 (7) ◽  
pp. 643-648 ◽  
Author(s):  
A. Stankiewicz ◽  
J. Winiarski ◽  
M. Stankiewicz ◽  
I. Szczygieł ◽  
B. Szczygieł
Keyword(s):  
Corrosion Resistance ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Machine Vision ◽  
Electrochemical Impedance ◽  
Composite Coatings ◽  
Resistance Evaluation

Effect of Doping of Nanoparticles on the Properties of Zn-Ni Composite Coatings

2018 ◽  
Vol 18 ◽  
pp. 19-26
Author(s):  
Nadjette Belhamra ◽  
Abd Raouf Boulebtina ◽  
Khadidja Belassadi ◽  
Abdelouahed Chala ◽  
Malika Diafi
Keyword(s):  
Corrosion Resistance ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Electrochemical Impedance ◽  
Steel Substrate ◽  
Composite Coatings ◽  
Alloy Coating ◽  
Corrosion Performance ◽  
X Ray ◽  
Ni Alloy

The purpose of this paper was to investigate the effect of Al2O3 and TiO2 nanoparticles contents on structural proporties, microhardness and corrosion resistance of Zn-Ni alloy coationg. Zn-Ni, Zn-Ni-Al2O3 and Zn-Ni-TiO2 composite coatings were electrodeposited on steel substrate by direct current in sulphate bath.The structure of the coatings was studied by X-ray diffration and by scaning electron miroscopy. The results showed the appearance of Ni5Zn21 phases and that the incrorporation of Al2O3 and TiO2 in the Zn-Ni coating refined the crystal grain size.The corrosion performance of coating in the 0.6M NaCl as a corrisive solution was investigated by potentiodynamic polarization and electrochemical impedance spectroscopy EIS methods. It was found that the incorporation of nanoparticules in Zn-Ni alloy coating have better corrosion resistance and the values of Rct and Zw increase, while the values of Cdl decrease with increasing of nanoparticules.

Electrochemical Impedance Spectroscopy (EIS) Study of Nano-Composite Polyurea Coating under the Wet-Dry Cyclic Conditions

2014 ◽  
Vol 789 ◽  
pp. 495-500
Author(s):  
Bing Ying Wang ◽  
Qing Hao Shi ◽  
Wen Long Zhang
Keyword(s):  
Corrosion Resistance ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Composite Coating ◽  
Electrochemical Impedance ◽  
Protective Action ◽  
Experimental Result ◽  
Resistance Property ◽  
Corrosion Resistance Property ◽  
Mass Fractions

The polyurea was modified by adding different amounts of nanometer ZnO. The corrosion behavior of polyurea/primer composite coating system in wet-dry cyclic environment of 3.5% NaCl solution was studied by using the Electrochemical Impedance Spectroscopy (EIS) measurement and adhesion test technology. The experimental result showed that, different mass fractions of nanometer ZnO had different influences on the corrosion resistance property of coating. When the mass fraction of nanometer ZnO was 5%, the composite coating had the largest protective action. The corrosion resistance property of nanometer ZnO can be improved by increasing the density of polyurea coating, however, the corrosion resistance property of polyurea coating will be weakened in case of exceeding the critical adding amount.

The effect of electroplating current density on microstructure, corrosion, and wear behavior of Ni–P–W–TiO2 coating

2021 ◽  
Vol 112 (6) ◽  
pp. 474-485
Author(s):  
Sajjad Sadeghi ◽  
Hadi Ebrahimifar
Keyword(s):  
Wear Resistance ◽  
Corrosion Resistance ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Current Density ◽  
Potentiodynamic Polarization ◽  
Electrochemical Impedance ◽  
Wear Behavior ◽  
Micro Hardness ◽  
Aisi 304L

Abstract The use of ceramic particles in the matrix of alloy coatings during the electroplating process has received considerable attention. These particles can create properties such as high corrosion resistance, insolubility, high-temperature stability, strong hardness, and self-lubrication capability. Herein, an Ni–P–W–TiO2 coating was deposited on an AISI 304L steel substrate using the electroplating method. Electroplating was performed at current densities of 10, 15, 20, and 25 mA · cm–2, and the effect of current density on microstructure, corrosion behavior, and wear behavior was investigated. The coatings were characterized by means of scanning electron microscopy. To investigate corrosion resistance, potentiodynamic polarization and electrochemical impedance spectroscopy tests were performed in a 3.5% NaCl aqueous solution. A pin-on-disk test was conducted to test the wear resistance of uncoated and coated samples. Sample micro-hardness was also measured by Vickers hardness testing. Examination of the microstructure revealed that the best coating was produced at a current density of 20 mA · cm–2. The results of potentiodynamic polarization and electrochemical impedance spectroscopy tests were consistent with microscopic images. The coating created at the current density of 20 mA · cm–2 had the highest corrosion resistance compared to other coated and non-coated samples. Furthermore, the results of the wear test showed that increasing the current density of the electroplating path up to 20 mA · cm–2 enhances micro-hardness and wear resistance.

Corrosion Resistance of a New Cu-Alloy (Low Ni) vis-à-vis Cu-10Ni Alloy in Sulfide Polluted Synthetic Seawater

2012 ◽  
Vol 585 ◽  
pp. 488-492
Author(s):  
Adeeba F. Khan ◽  
Awanikumar P. Patil ◽  
T. Subba Rao
Keyword(s):  
Corrosion Resistance ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Electrochemical Impedance ◽  
Accelerated Corrosion ◽  
Synthetic Seawater ◽  
Cu Alloy

Cu-10Ni alloy suffers accelerated corrosion in sulfide polluted seawater. As an alternative, a new single phased, Cu-28%Zn-5%Ni-5%Mn-2%Fe alloy (hereby referred as CNZ-alloy) is developed and tested for the corrosion resistance in clean and sulfide polluted synthetic seawater. The CNZ-alloy showed better corrosion resistance than the standard Cu-10Ni alloy in both the test solutions i.e. clean and sulfide polluted synthetic seawater with . The results are discussed on the basis of polarization and electrochemical impedance spectroscopy. The better corrosion resistance of CNZ-alloy is attributed to the formation of protective ZnS and MnS2 films.

Sign in / Sign up

Export Citation Format

Share Document