Dispersions based on hexagonal boron nitride, h-BN, nanoparticles, at 0.50, 0.75 and 1.0 wt.% mass concentrations, in an ester base oil composed mainly of trimethylolpropane trioleate, were investigated as potential nanolubricants. The stability of the dispersions was assessed to determine the reliability of the tribological, thermophysical and rheological measurements. Density and viscosity were measured from 278.15 to 373.15 K, while rheological behavior was analyzed at shear rates from 1 to 1000 s−1 at 283.15 K. Newtonian behavior was exhibited by all nanolubricants at the explored conditions, with the exception of the highest concentration at the lowest shear rates, where possible non-Newtonian behavior was observed. Tribological tests were performed under a normal load of 2.5 N. Wear was evaluated by means of a 3D profiler, scanning electron microscopy and confocal Raman microscopy. The best tribological performance was achieved by the 0.75 wt.% nanolubricant, with reductions of 25% in the friction coefficient, 9% in the scar width, 14% in the scar depth, and 22% of the transversal area, all with respect to the neat oil. It was observed that physical protective tribofilms are created between rubbing surfaces.
Tribological properties of hexagonal boron nitride nanoparticles or graphene nanoplatelets blended with an ionic liquid as additives of an ester base oil