scholarly journals Analysis of defects in a twin roll cast Mg‐Y‐Zn magnesium alloy

2021 ◽  
Author(s):  
Kristina Kittner ◽  
Madlen Ullmann ◽  
Falko Arndt ◽  
Susanne Berndorf ◽  
Thorsten Henseler ◽  
...  
Keyword(s):  
Magnesium Alloy ◽  
Twin Roll Cast ◽  
Twin Roll

An XPS Study of Native Oxide and Isothermal Oxidation Kinetics at 300 °C of AZ31 Twin Roll Cast Magnesium Alloy

2013 ◽  
Vol 81 (5-6) ◽  
pp. 529-548 ◽  
Author(s):  
H. Saleh ◽  
T. Weling ◽  
J. Seidel ◽  
M. Schmidtchen ◽  
R. Kawalla ◽  
...  
Keyword(s):  
Magnesium Alloy ◽  
Oxidation Kinetics ◽  
Isothermal Oxidation ◽  
Native Oxide ◽  
Cast Magnesium Alloy ◽  
Cast Magnesium ◽  
Xps Study ◽  
Twin Roll Cast ◽  
Twin Roll

scholarly journals Determination of the Hot Cracking Tendency of a Twin-Roll Cast AZ31 Magnesium Alloy by Means of Gleeble Tests

2018 ◽  
Vol 918 ◽  
pp. 40-47
Author(s):  
Heike Wemme ◽  
Christina Krbetschek ◽  
Madlen Ullmann ◽  
Anna Freigang ◽  
Stefan Plach ◽  
...  
Keyword(s):  
Magnesium Alloy ◽  
Az31 Alloy ◽  
Hot Cracking ◽  
Az31 Magnesium Alloy ◽  
Cast Magnesium ◽  
Twin Roll Cast ◽  
Twin Roll ◽  
Cracking Tendency

The knowledge about the formation of hot cracking in magnesium alloys, such as in twin-roll cast magnesium sheets and strips, is fundamental for a good quality of the strips during the further processing by rolling or welding and minimize the reject. Hot cracking often occurs in the so-called mushy zone, when solid phases and melt coexist, at temperatures where the material no longer exhibits ductility. For the evaluation of the hot cracking tendency of an alloy, the width of the HTBR (High-temperature brittleness range) can be used. On the basis of a test on a Gleeble HDS-V40, the HTBR was determined for a twin-roll cast AZ31 magnesium alloy. The transition between ductile forming behaviour and complete brittle reaction of the AZ31 alloy is confirmed by the observation of the fracture surfaces (determination of the fracture type) in the scanning electron microscope (SEM) and is located at 555 °C. The HTBR shows a range 35 K.

Influence of Lead on the Microstructure and Corrosion Behavior of Melt-Conditioned, Twin-Roll-Cast AZ91D Magnesium Alloy

CORROSION ◽  
2012 ◽  
Vol 68 (6) ◽  
pp. 548-556 ◽  
Author(s):  
S. Pawar ◽  
X. Zhou ◽  
G.E. Thompson ◽  
J.D. Robson ◽  
I. Bayandorian ◽  
...  
Keyword(s):  
Magnesium Alloy ◽  
Corrosion Behavior ◽  
Az91d Magnesium Alloy ◽  
Twin Roll Cast ◽  
Twin Roll

Effect of rolling temperature on microstructure and texture of twin roll cast ZK60 magnesium alloy

2010 ◽  
Vol 20 (11) ◽  
pp. 2086-2091 ◽  
Author(s):  
Hong-mei CHEN ◽  
Hua-shun YU ◽  
Suk-bong KANG ◽  
Guang-hui MIN ◽  
Yun-xue JIN
Keyword(s):  
Magnesium Alloy ◽  
Rolling Temperature ◽  
Twin Roll Cast ◽  
Zk60 Magnesium Alloy ◽  
Twin Roll
Sign in / Sign up

Export Citation Format

Share Document