Multiple copper-zinc alloy was used to treat water in order to restrict the formation of hard scale during heating process. Trace amounts of metal ions were dissolved from the alloy under the action of tiny battery corrosion, which took part in the crystallization of calcium carbonate crystal. The ion migration rules and its effect on the crystal structure of water scale were studied. The ICP test results show that after immersion in the water for 20 min, the zinc ion concentration increased to 0.35 mg•L-1 compared with contrast group. The simulating experiment of the scale crystal growth demonstrated that the calcium carbonate scale after treated with the alloy showed a transformation from calcite to aragonite, and the ratio of calcite to aragonite changed from 1:0.125 to 1:2.30. Meanwhile, the heat transfer efficiency was increased to 2.19%.