Effect of modified rubber powder on the morphology and thermal and mechanical properties of blown poly(lactic acid)-hydroxyl epoxidized natural rubber films for flexible film packaging

2019 ◽  
Vol 136 (21) ◽  
pp. 47503 ◽  
Author(s):  
Chor Wayakron Phetphaisit ◽  
Wittawat Wapanyakul ◽  
Pranee Phinyocheep
Keyword(s):  
Mechanical Properties ◽  
Lactic Acid ◽  
Natural Rubber ◽  
Epoxidized Natural Rubber ◽  
Poly Lactic Acid ◽  
Thermal And Mechanical Properties ◽  
Rubber Powder ◽  
Flexible Film

scholarly journals The effect of dynamic vulcanization on the morphological and mechanical properties of the toughened poly (lactic acid)/epoxidized natural rubber

2018 ◽  
Vol 14 (3) ◽  
pp. 348-352 ◽  
Author(s):  
Nur Amira Sahirah Abdullah ◽  
Zurina Mohamad
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Lactic Acid ◽  
Impact Strength ◽  
Natural Rubber ◽  
Crosslinking Agent ◽  
Epoxidized Natural Rubber ◽  
Poly Lactic Acid ◽  
Dynamic Vulcanization ◽  
The Impact

Poly (lactic acid)/epoxidized natural rubber (PLA/ENR) was prepared by using counter-rotating twin-screw extruder. For dynamic vulcanization process, ENR was compounded with 3 phr of N, N’-m-phenylenebismaleimide (HVA-2) as a crosslinking agent. The aim of this study is to determine the effect of unvulcanized and dynamically vulcanized of ENR on the properties of PLA/ENR blend. The blending of PLA with ENR was prepared with the various composition of ENR (0 wt% to 30 wt%). The morphology and mechanical properties of the blends were investigated by using scanning electron microscope (SEM), tensile test, and impact test. The unvulcanized blend produced a co-continuous morphology of PLA and ENR and the dynamically vulcanized blend shows the dispersed ENR rubber particles in PLA continuous matrix.  For both systems, the tensile strength value was dropped with the increasing amount of ENR content. The impact strength of both systems shows the maximum value at 20 wt% of ENR content. However, dynamically vulcanized PLA/ENR blend shows a better tensile strength and impact strength value as compared with unvulcanized blend.

Thermal and Mechanical Properties of Mulch Film from Poly(Lactic Acid)/Expoxidized Natural Rubber Blends Filled with Rutile TiO2 as Fillers

2013 ◽  
Vol 844 ◽  
pp. 65-68
Author(s):  
Pranee Nuinu ◽  
Kittikorn Samosorn ◽  
Kittisak Srilatong ◽  
Siripa Tongbut ◽  
Sayant Saengsuwan
Keyword(s):  
Thin Film ◽  
Mechanical Properties ◽  
Thermal Stability ◽  
Lactic Acid ◽  
Thermal Properties ◽  
Natural Rubber ◽  
Decomposition Temperature ◽  
Poly Lactic Acid ◽  
Thermal And Mechanical Properties ◽  
Thermal Stability Of

The aim of this research was to reduce and improve the brittleness and thermal properties of poly lactic acid (PLA), respectively. Epoxidized natural rubber (ENR) was used to enhance the toughness and rutile titanium dioxide (R-TiO2) as filler was also incorporated to improve the thermal properties of the PLA. 10wt% ENR with epoxidation contents of 25 mol% (ENR25) and 50 mol% (ENR50) and various R-TiO2contents (0-10 phr)were compounded with PLA by using a twin-screw extruder at 155-165°C and a rotor speed of 40 rpm. The pellets of blends were then formed a thin film using a cast film extruder machine and cooled down under air flow. Thermal and mechanical properties and morphology of PLA/ENR/R-TiO2thin film were investigated. The crystallinity of PLA was found to increase with addition of ENR. The mechanical properties of thin film showed that the ENR50 enhanced the elongation but reduced the tensile strength of PLA with addition of R-TiO2at 5 and 10 phr, respectively. The TGA indicated that the addition of 10 phr R-TiO2increased in the decomposition temperature at 5% weight loss (Td5%) of PLA/ENR film. Thus the thermal stability of PLA/ENR50 was found to improve with addition of R-TiO2. From morphology study, the ENR50 phase showed a good dispersion in the PLA matrix. In conclusion, the addition of ENR and R-TiO2was found to enhance both toughness and thermal stability of PLA.

scholarly journals Biocomposites of Epoxidized Natural Rubber/Poly(lactic acid) Modified with Natural Fillers (Part I)

2021 ◽  
Vol 22 (6) ◽  
pp. 3150
Author(s):  
Anna Masek ◽  
Stefan Cichosz ◽  
Małgorzata Piotrowska
Keyword(s):  
Tensile Strength ◽  
Lactic Acid ◽  
Natural Rubber ◽  
Epoxidized Natural Rubber ◽  
Poly Lactic Acid ◽  
Uv Aging ◽  
High Elasticity ◽  
Natural Fillers ◽  
Natural Additives

The study aimed to prepare sustainable and degradable elastic blends of epoxidized natural rubber (ENR) with poly(lactic acid) (PLA) that were reinforced with flax fiber (FF) and montmorillonite (MMT), simultaneously filling the gap in the literature regarding the PLA-containing polymer blends filled with natural additives. The performed study reveals that FF incorporation into ENR/PLA blend may cause a significant improvement in tensile strength from (10 ± 1) MPa for the reference material to (19 ± 2) MPa for the fibers-filled blend. Additionally, it was found that MMT employment in the role of the filler might contribute to ENR/PLA plasticization and considerably promote the blend elongation up to 600%. This proves the successful creation of the unique and eco-friendly PLA-containing polymer blend exhibiting high elasticity. Moreover, thanks to the performed accelerated thermo-oxidative and ultraviolet (UV) aging, it was established that MMT incorporation may delay the degradation of ENR/PLA blends under the abovementioned conditions. Additionally, mold tests revealed that plant-derived fiber addition might highly enhance the ENR/PLA blend’s biodeterioration potential enabling faster and more efficient growth of microorganisms. Therefore, materials presented in this research may become competitive and eco-friendly alternatives to commonly utilized petro-based polymeric products.

Effect of the Introduction of Fish Collagen on the Thermal and Mechanical Properties of Poly(lactic acid)

2015 ◽  
Vol 54 (43) ◽  
pp. 10945-10951 ◽  
Author(s):  
Hui Ma ◽  
Jiajia Shen ◽  
Qun Yang ◽  
Jie Zhou ◽  
Shuangshuang Xia ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Lactic Acid ◽  
Poly Lactic Acid ◽  
Thermal And Mechanical Properties ◽  
Fish Collagen
Sign in / Sign up

Export Citation Format

Share Document